Fracture resistance and marginal fit of the zirconia crowns with varied occlusal thickness.

PURPOSE: The present study aimed to evaluate the clinical applicability of monolithic zirconia (MZ) crowns of different thickness via determination of fracture resistance and marginal fit. MATERIALS AND METHODS: MZ crowns with 0.5, 0.8, 1.0, and 1.5 mm thickness and porcelain fused to metal (PFM) crowns were prepared, ten crowns in each group. Marginal gaps of the crowns were measured. All crowns were aged with thermal cycling (5 - 55℃/10000 cycle) and chewing simulator (50 N/1 Hz/lateral movement: 2 mm, mouth opening: 2 mm/240000 cycles). After aging, fracture resistance of crowns was determined. Statistical analysis was performed with one-way ANOVA and Tukey's HDS post hoc test. RESULTS: Fracture loads were higher in the PFM and 1 mm MZ crowns compared to 0.5 mm and 0.8 mm crowns. 1.5 mm MZ crowns were not broken even with the highest force applied (10 kN). All marginal gap values were below 86 µm even in the PFM crowns, and PFM crowns had a higher marginal gap than the MZ crowns. CONCLUSION: The monolithic zirconia exhibited high fracture resistance and good marginal fit even with the 0.5 mm thickness, which might be used with reduced occlusal thickness and be beneficial in challengingly narrow interocclusal space.

Determination of the effective anticandidal concentration of denture cleanser tablets on some denture base resins.

Although the effectiveness of chemical cleansing against Candida albicans biofilm has been shown, the effective concentration of denture cleanser tablets has not been studied. The aim of this study was to assess the effect of three denture materials against Candida albicans biofilm and to determine effective concentrations of denture cleanser tablets. The surface-roughness of Acron-hi™, QC-20™ and Deflex™ (n=45 per resin) resins was standardized by using a profilometer and their contact angle or surface free energy was calculated. C. albicans biofilm was formed on all three resins and were treated with Polident 3 min™, Corega™ and Fittydent™ cleanser solutions at various concentrations and both resin-biofilm and cleanser-biofilm interest were determined by using a MTT protocol according to the European Committee on Antimicrobial Susceptibility Testing's antifungal susceptibility testing (AFST-EUCAST). Scanning electron microscopy was used to compare the efficacy of different resin materials against C. albicans biofilm. Anticandidal activity and surface free energy statistical parameters were calculated by using 3-way and 1-way ANOVA, respectively (p<0.05). Polident 3 min™ and Corega™ tablets significantly inhibited (p<0.05) the proliferation of C. albicans against all denture resins at 27-37 mg/mL. Scanning electron microscopy results indicated that there was no significant difference among resin specimens regarding biofilm formation on dentures. We failed to find a significant relationship between surface free energy and the anticandidal effect of resin types. However, the polarity value of the resins was statistically associated with their anticandidal activity. The polarity of the resins, the concentrations of tablets and the chemical content of the cleanser may directly affect C. albicans biofilm formations. Polident 3 min™ and Corega™ tablets should be suggested for patients who use any denture resin types, whereas the Fittydent™ tablet should only be proposed for those who use Deflex™, when two tablets are dropped into 150 mL water.

Determination of the effective anticandidal concentration of denture cleanser tablets on some denture base resins

Abstract Objective Although the effectiveness of chemical cleansing against Candida albicans biofilm has been shown, the effective concentration of denture cleanser tablets has not been studied. The aim of this study was to assess the effect of three denture materials against Candida albicans biofilm and to determine effective concentrations of denture cleanser tablets. Material and methods The surface-roughness of Acron-hi™, QC-20™ and Deflex™ (n=45 per resin) resins was standardized by using a profilometer and their contact angle or surface free energy was calculated. C. albicans biofilm was formed on all three resins and were treated with Polident 3 min™, Corega™ and Fittydent™ cleanser solutions at various concentrations and both resin-biofilm and cleanser-biofilm interest were determined by using a MTT protocol according to the European Committee on Antimicrobial Susceptibility Testing's antifungal susceptibility testing (AFST-EUCAST). Scanning electron microscopy was used to compare the efficacy of different resin materials against C. albicans biofilm. Anticandidal activity and surface free energy statistical parameters were calculated by using 3-way and 1-way ANOVA, respectively (p<0.05). Results Polident 3 min™ and Corega™ tablets significantly inhibited (p<0.05) the proliferation of C. albicans against all denture resins at 27-37 mg/mL. Scanning electron microscopy results indicated that there was no significant difference among resin specimens regarding biofilm formation on dentures. We failed to find a significant relationship between surface free energy and the anticandidal effect of resin types. However, the polarity value of the resins was statistically associated with their anticandidal activity. Conclusions The polarity of the resins, the concentrations of tablets and the chemical content of the cleanser may directly affect C. albicans biofilm formations. Polident 3 min™ and Corega™ tablets should be suggested for patients who use any denture resin types, whereas the Fittydent™ tablet should only be proposed for those who use Deflex™, when two tablets are dropped into 150 mL water.